Crystal structures of three CaSeO₄ polymorphs and their mineralogical relationships

Autor(en)

Helmut Pristacz, Dominik Talla, Frederik Preuschl, Gerald Giester, Manfred Wildner

Abstrakt

Three polymorphs of anhydrous calcium selenate CaSeO4 have been synthesized; the orthorhombic as well as the monoclinic polymorph were prepared at 210 °C; crystals of tetragonal CaSeO4 were grown at 70 °C.,,Based on single crystal X-ray diffraction data the structure of the orthorhombic compound was solved and refined in space group Cmca [a = 7.192(1), b = 14.404(2), c = 6.398(1) Å, V = 662.8 Å3, Z = 8 to R1 = 2.0 %, wR2 = 5.5 %]. It belongs to a new structure type with close resemblance to zircon and anhydrite. The structure of monoclinic CaSeO4 is isotypic with monazite and was refined in space group P21/n[a = 6.860(1), b = 7.086(1), c = 6.692(1) Å, ß = 104.21(1)°, V = 315.3 Å3, Z = 4; R1 = 2.6 %, wR2 = 5.2 %]. The tetragonal modification, refined in space group I41/a, (a = 5.054(1), c = 11.678(2) Å, V = 298.3 Å3, Z = 4; R1 = 1.6 %, wR2 = 4.1 %) represents a scheelite structure type.,,In addition, structure relationships within A[8]X[4]O4 representatives are emphasized.

Organisation(en)

Institut für Mineralogie und Kristallographie

Journal

Neues Jahrbuch für Mineralogie. Abhandlungen

Band

191

Seiten

215-223

Anzahl der Seiten

9

ISSN

0077-7757

Publikationsdatum

2014

Peer-reviewed

Ja

ÖFOS 2012

105113 Kristallographie, 105116 Mineralogie

Link zum Portal

https://ucrisportal.univie.ac.at/de/publications/dd52a614-0103-4732-8195-be179c365ce0