Crystal structures, site occupations and phase equilibria in the system V-Zr-Ge
- Author(s)
- Martin Marker, Herta Silvia Effenberger, Klaus Richter
- Abstract
The V-Zr-Ge system was studied for two isothermal sections at 900 and 1200 °C. Three ternary compounds VZrGe (tI12, I4/mmm, CeScSi-type), VxZr5-xGe4 (oP36, Pnma, Sm5Ge4-type) and V4+xZr2-xGe5 (oI44, Ibam, Si5V6-type) were structurally characterized. Optical microscopy and powder X-ray diffraction (XRD) were used for initial sample characterization and electron probe microanalysis (EPMA) of the annealed samples was used to determine the exact phase compositions. The variation of the cell parameters of the various ternary solid solutions with the composition was determined. The three ternary phases were structurally characterized by means of single crystal and powder XRD. While VZrGe is almost a line compound, VxZr5-xGe4 (0.2 ? x ? 3.0) and V4+xZr2-xGe5 (0.06 ? x ? 1.2) are forming extended solid solution ranges stabilized by differential fractional site occupancy of V and Zr on the metal sites.
- Organisation(s)
- Department of Functional Materials and Catalysis, Department of Mineralogy and Crystallography
- Journal
- Solid State Sciences
- Volume
- 11
- Pages
- 1475-1483
- No. of pages
- 9
- ISSN
- 1293-2558
- DOI
- https://doi.org/10.1016/j.solidstatesciences.2009.05.005
- Publication date
- 2009
- Peer reviewed
- Yes
- Austrian Fields of Science 2012
- 104003 Inorganic chemistry, 105113 Crystallography, 104011 Materials chemistry
- Portal url
- https://ucrisportal.univie.ac.at/en/publications/450c7349-c3ad-4c55-8e08-7b4e23e93f05